Índices fisicoquímicos de la boquilla superior de la cuchara
Item |
RS-SSK-1 |
RS-SSK-2 |
RS-SSK-3 |
RS-SSK-4 |
Al2O3 % ≥ |
80 |
75 |
60 |
65 |
MgO % ≥ |
/ |
/ |
/ |
C % |
≤6 |
≤6 |
4 |
4 |
Bulk density g/cm3 ≥ |
2.9 |
2.8 |
2.6 |
2.65 |
Modulus of rupture Mpa ≤ |
15 |
15 |
15 |
15 |
Crushing strength Mpa ≥ |
70 |
60 |
40 |
25 |
Boquilla inferior cuchara
Las materias primas de la boquilla inferior de la serie RS son corindón, bauxita con alto contenido de alúmina, grafito en escamas, antioxidante, resina fenólica, etc. Características de las boquillas inferiores en buena resistencia al choque térmico, fuerte resistencia a la corrosión erosiva, buena resistencia a la ruptura, etc.
Item |
RS-XSK-1 |
RS-XSK-2 |
RS-XSK-3 |
RS-XSK-4 |
RS-XSK-5 |
Al2O3 % ≥ |
75 |
55 |
68 |
60 |
65 |
MgO % ≥ |
/ |
/ |
/ |
/ |
C % |
6 |
5 |
4 |
4 |
4 |
Bulk density g/cm3 ≥ |
2.8 |
2.6 |
2.7 |
2.7 |
2.65 |
Apparent porosity % ≤ |
15 |
15 |
15 |
15 |
15 |
Crushing strength Mpa ≥ |
60 |
40 |
40 |
40 |
25 |
Boquilla larga (cubierta de la cuchara)
La boquilla larga es refractaria funcional que conecta la cuchara y la artesa. La boquilla larga desempeña el papel de estabilizar el estado del flujo del líquido del acero, evitando la oxidación del líquido del acero, evitando que el líquido del acero salpique, etc. pronto. Además, las boquillas largas RS también cuentan con una operación conveniente, una mejora significativa de las condiciones de trabajo.
Índices fisicoquímicos de boquilla largos
Item |
RS-CSK-1 |
RS-CSK-2 |
RS-CSK-3 |
RS-CSK-4 |
RS-CSK-5 |
Main body |
Slag line |
Main body |
Slag line |
Al2O3 % |
45 |
/ |
45 |
35 |
40 |
50 |
SiO2 % |
20 |
/ |
20 |
25 |
20 |
10 |
C+SiC % |
25 |
25 |
25 |
40 |
25 |
25 |
ZrO2 % |
/ |
60 |
/ |
/ |
/ |
/ |
Bulk density g/cm3 ≥ |
2.3 |
3 |
2.3 |
2 |
2.25 |
2.3 |
Apparent porosity % |
20 |
19 |
20 |
19 |
23 |
20 |
Crushing strength Mpa ≥ |
22 |
10 |
22 |
10 |
22 |
22 |
Cold modulus of rupture Mpa ≥ |
6 |
4 |
6 |
4 |
6 |
6 |
Thermal shock resistance (1100℃, water cooling)/times |
5 |
5 |
5 |
5 |
Boquilla de entrada sumergida
La boquilla de entrada sumergida desempeña el papel de evitar que el líquido de acero se oxide cuando fluye de la artesa al cristalizador, además, también tiene la función de distribuir uniformemente el líquido de acero al cristalizador y controlar el estado de flujo del líquido de acero en el cristalizador. La boquilla sumergida de la serie RS tiene buena resistencia a la corrosión de la escoria, resistencia al bloqueo, larga vida útil, baja tasa de accidentes, etc.
Índices fisicoquímicos de la boquilla de entrada sumergida
Item |
RS-JSK-1 |
RS-CSK-2 |
RS-CSK-3 |
Main body |
Slag line |
Main body |
Slag line |
Main body |
Slag line |
Al2O3 % ≥ |
40 |
/ |
45 |
/ |
35 |
/ |
SiO2 % ≤ |
20 |
/ |
15 |
/ |
25 |
/ |
C+SiC % |
≥25 |
≥13 |
≥22 |
≥13 |
≤40 |
≤25 |
ZrO2 % |
/ |
70 |
/ |
75 |
/ |
60 |
Bulk density g/cm3 ≥ |
2.2 |
3.4 |
2.3 |
3.55 |
2 |
3 |
Apparent porosity %≤ |
20 |
19 |
18 |
18 |
19 |
19 |
Crushing strength Mpa ≥ |
20 |
20 |
20 |
14 |
10 |
10 |
Cold modulus of rupture Mpa ≥ |
6 |
5 |
8 |
5 |
4 |
4 |
Thermal shock resistance (1100℃, water cooling)/times |
5 |
5 |
5 |
Boquilla superior de artesa
La boquilla superior de la artesa se inserta en el bloque del pozo durante el uso, puede controlar el flujo de líquido de acero combinado con el tapón. La boquilla superior de artesa de la serie RS tiene una excelente resistencia al lavado, buena estabilidad al choque térmico, buena resistencia a la corrosión y resistencia al bloqueo. Cuando se combina con el tapón integral de la serie RS, los tiempos de colada continua de la artesa se pueden aumentar significativamente.
Item |
RS-HBZ-A R |
RS-HBZ-B |
Chemical composition(%) ≥ |
Al2O3 |
55 |
60 |
ZrO2 |
5 |
5 |
C |
3 |
8 |
Bulk density g.cm3 ≥ |
2.85 |
2.85 |
Apparent porosity % ≤ |
15 |
15 |
Crushing strength Mpa ≥ |
60 |
40 |
Índices fisicoquímicos de la tobera superior de la artesa
Item |
RS-ZSK-1 |
RS-ZSK-2 |
RS-ZSK-3 |
Main body |
Bowl part |
Main body |
Bowl part |
Main body |
Bowl part |
Al2O3 % ≥ |
45 |
65 |
45 |
50 |
45 |
/ |
SiO2 % ≤ |
15 |
10 |
15 |
5 |
15 |
/ |
C+SiC % ≥ |
22 |
10 |
22 |
≤20 |
22 |
≤20 |
MgO % ≥ |
/ |
/ |
/ |
15 |
/ |
60 |
Bulk density g/cm3 ≥ |
2.3 |
2.7 |
2.3 |
2.3 |
2.3 |
2.6 |
Apparent porosity %≤ |
18 |
16 |
18 |
17 |
18 |
19 |
Crushing strength Mpa ≥ |
20 |
25 |
20 |
20 |
20 |
15 |
Cold modulus of rupture Mpa ≥ |
8 |
8 |
8 |
10 |
8 |
5 |
Thermal shock resistance (1100℃, water cooling)/times |
≥5 |
≥5 |
≥5 |
Tundish boquilla superior porosa
Para evitar el bloqueo, la vida útil de la boquilla superior de artesa tradicional y la boquilla sumergida es corta. Por lo tanto, se desarrolla una boquilla superior de artesa porosa para superar esta deficiencia. Según la estructura y función, las boquillas superiores porosas de artesa se clasifican en boquillas superiores porosas que no cambian rápidamente y boquillas superiores porosas que cambian rápidamente (la boquilla sumergida se puede cambiar rápidamente para prometer la consistencia de la fundición). La boquilla superior especialmente porosa de cambio rápido puede aumentar significativamente la vida útil de la artesa, aunque la vida útil de la boquilla sumergida es relativamente baja. La vida útil de la artesa de losa utilizada actualmente es superior a 10 horas.
Item |
RS-TZSK-1 |
RS-TZSK-2 |
RS-TZSK-3 |
Main body |
Bowl part |
Porous inner lining |
Main body |
Bowl part |
porous inner lining |
Al2O3 % ≥ |
45 |
65 |
55 |
65 |
50 |
50 |
50 |
SiO2 % ≤ |
25 |
10 |
5 |
10 |
10 |
5 |
10 |
C+SiC % ≥ |
25 |
10 |
20 |
/ |
22 |
≤20 |
22 |
MgO % ≥ |
/ |
/ |
/ |
/ |
/ |
15 |
/ |
Bulk density g/cm3 ≥ |
2.2 |
2.7 |
2.4 |
2.3 |
2.4 |
2.3 |
2.4 |
Apparent porosity %≤ |
20 |
16 |
25 |
16 |
18 |
17 |
18 |
Crushing strength Mpa ≥ |
22 |
25 |
20 |
40 |
20 |
20 |
20 |
Modulus of rupture Mpa ≥ |
5 |
8 |
5 |
/ |
8 |
10 |
8 |
Thermal shock resistance (1100℃, water cooling)/times |
≥5 |
/ |
≥5 |
Boquilla dosificadora
Las boquillas dosificadoras adoptan principalmente el método de inserción y se clasifican en boquillas dosificadoras ordinarias y boquillas dosificadoras de cambio rápido. La composición química principal del núcleo de la boquilla es zirconia, por lo que la boquilla dosificadora tiene alta refractariedad, buena resistencia al choque térmico, buena resistencia a la corrosión, resistencia al lavado, pequeño agrandamiento del orificio de la boquilla, larga vida útil, etc. Confiando en el sistema de cambio rápido, las boquillas multi-inferiores se pueden reemplazar durante la fundición de artesa, por lo que el servicio de la artesa se prolonga y se mejora la eficiencia de la fundición.
Índices fisicoquímicos del núcleo interno de la boquilla dosificadora regular
Item |
RS-DSK-1 |
RS-DSK-2 |
RS-DSK-3 |
RS-DSK-4 |
RS-DSK-5 |
RS-DSK-6 |
ZrO2+HfO2 ≥ |
64 |
69 |
79 |
89 |
93 |
94 |
Bulk density g/cm3 ≥ |
3.6 |
3.7 |
3.9 |
4.2 |
4.3 |
4.3 |
Apparent porosity %≤ |
23 |
23 |
23 |
23 |
21 |
21 |
Crushing strength Mpa ≥ |
80 |
80 |
80 |
80 |
100 |
100 |
Refractoriness ℃ > |
1790 |
1790 |
1790 |
1790 |
1790 |
1790 |